Cu-Fe-P合金の粒子分散と耐熱性(<特集>複合材料)
- フォーマット:
- 論文
- 責任表示:
- 北, 和久 ; 小林, 一徳 ; 門前, 亮一
- 言語:
- 日本語
- 出版情報:
- 日本材料学会, 2000-05-15
- 著者名:
- 掲載情報:
- 材料 = Journal of the Society of Materials Science, Japan
- ISSN:
- 0514-5163
- 巻:
- 49
- 通号:
- 5
- 開始ページ:
- 482
- 終了ページ:
- 487
- バージョン:
- publisher
- 概要:
- 金沢大学理工研究域機械工学系<br />The influence of dispersions of particles on the recrystallization behavior has been examined in industrially processed specimens of a Cu-Fe-P alloy(CDA194). The specimens are produced through the steps of hot roll … ing, cold rolling, aging and final cold rolling. The γ→α martensitic transformation of small coherent γ-Fe precipitate particles which form on decreasing temperature during hot rolling is induced by subsequent cold rolling. Aging following the cold rolling produces fine γ-Fe particles, which are transformed to α-Fe by final cold rolling. The nucleation of recrystallization occurs predominantly at coarse Fe_3P particles, observed after the hot rolling, larger than about 1μm in diameter. A denser dispersion of smaller α-Fe particles shows a larger retarding effect on grain-boundary migration. A specimen with smaller α-Fe and smaller Fe_3P particles has a higher heat resistance and a higher strength. 続きを見る
- URL:
- http://hdl.handle.net/2297/12172
類似資料:
日本材料学会 |
[門前亮一] |
金沢大学理工研究域機械工学系 | |
日本材料学会 = The Society of Materials Science, Japan | |
|
金沢大学理工研究域機械工学系 |
金沢大学理工研究域機械工学系 |
金属社 |
金沢大学 |
[門前亮一] |