高張力低合金鋼切欠き平板における応力腐食割れの発生と成長
- フォーマット:
- 論文
- 責任表示:
- 広瀬, 幸雄 ; 田中, 啓介 ; 岡林, 邦夫
- 言語:
- 日本語
- 出版情報:
- 日本材料学会, 1978-06-15
- 著者名:
- 掲載情報:
- 材料=Journal of the Society of Materials Science, Japan
- ISSN:
- 0514-5163
- 巻:
- 27
- 通号:
- 297
- 開始ページ:
- 545
- 終了ページ:
- 551
- バージョン:
- publisher
- 概要:
- 金沢大学大学院自然科学研究科<br />Stress corrosion tests were conducted on the notched plates of SNCM 8 steel tempered at low temperatures in 3.5% NaCl solution environment. The effects of notch radius and plate thickness on nucleation and growth o … f cracks were analysed from a viewpoint of fracture mechanics. The results obtained are summarized as follows : (1) The time to crack nucleation at the notch root t_n was correlated to the notch radius ρ and the stress intensity factor K_0 by the following equation: t_n= 5.8 x 10^<27>(K_0/√<ρ>)^<-12.5> (2) The relation between crack growth rate and stress intensity factor was divided into three regions I, II and III. In regions II and III, the growth rate was found to be higher in thicker specimens than in thinner ones, while there was no thickness effect on growth rate in region I including K_<ISCC> (3) Scanning electron microscopic observations of fracture surfaces indicated that intergranular fracture along prior austenite grain boundaries was predominant in the region of low stress intensity factors and that the fraction of grain boundary fracture area in the total fracture surface decreased with increasing stress intensity factor. 続きを見る
- URL:
- http://hdl.handle.net/2297/12311
類似資料:
日本材料学会 |
日本材料学会 |
日本材料学会 | |
日本材料学会 |
日本材料学会 |
日本材料学会 |
日本材料学会 |
日本材料学会 |
日本材料学会 |
日本材料学会 |
日本材料学会 |