論文 |
論文
|
田中, 隆太郎 ; 林, 勇伝 ; 田邉, 一真 ; 上田, 隆司 ; 細川, 晃
概要:
This study deals with the trial for improvement of chip controllability in turning with selective laser heat treatment for workpiece. Selective heat treatment for carbon steel JIS S45C was carried out with Nd:YAG laser which
…
could be transmitted through an optical fiber and shows higher absorption rate against carbon steels than CO2 laser. In turning of these selective laser heat threatened carbon steel, the chip form changed regular curl from irregular curl and chip breakability was improved compared with non-laser treated carbon steel. Surface roughness was obviously smaller comparing with non-laser treated carbon steel. Especially in the case that the depth of cut was larger, the surface roughness was smaller. As for cutting force, the principal force was slightly smaller, but the thrust force and feed force were almost the same. The cutting temperature was slightly lower. The tool wear was almost same as that in the case of non-laser treated carbon steel.
続きを見る
|
||||
| 2.
論文 |
論文
|
鬼頭, 昂志 ; 田中, 隆太郎 ; 細川, 晃 ; 上田, 隆司 ; 古本, 達明
概要:
著者らが提案した，レーザを用いた被削材の部分的熱処理によるバリの抑制方法について，より効率的なバリの抑制を実現するために，フライスカッタの出口角度，送り速度，切削速度およびレーザ照射強度が切削後の端部形状におよぼす影響を調査した．その結果，
…
切削後の被削材端部の形状は，カッタ出口角度と送り速度によって定まる切取り厚さと，カッタ出口角度と切削速度によって定まる熱処理部の切削時間に依存することが明らかとなった．また，レーザ照射条件を制御して深いマルテンサイト層を生成することによって，より確実にバリの発生を抑制することができることが明らかとなった．
続きを見る
|
||||
| 3.
論文 |
論文
|
田中, 隆太郎 ; 鬼頭, 昴志 ; 細川, 晃 ; 上田, 隆司 ; 古本, 達明
概要:
本研究では，炭素鋼の正面フライス加工において，加工能率を維持したままバリの抑制を図る手法として，レーザを用いた被削材の部分的な改質による方法について提案した．実験では炭酸ガスレーザを用いて選択的に熱処理を行った炭素鋼JIS S45Cの正面フ
…
ライス加工において，切削後の被削材端部の形状についてバリの高さの測定と断面の組織観察を行い，被削材へのレーザ熱処理によるバリの抑制効果について検討を行った．切削後における被削材の端部の形状はレーザ照射条件に依存し，表層にマルテンサイト組織が生成されていると微小なコバ欠けが生じる．またマルテンサイト組織が生成されていなくても，レーザ熱処理により硬度が母材よりも高くなっていると発生するバリの高さが小さくなる．最終切取り予定線へレーザ熱処理を行えば, それ以前の切削でバリが発生していても最終切削においてバリの発生を抑制することができる．仕上げ面粗さは，レーザ熱処理の影響をほとんど受けない．
続きを見る
|